Because fluorosilicone rubber is expensive, the rubber is easy to contaminate, thus affecting the performance, so the production of fluorosilicone rubber operation process is extremely strict.
1, keep the production environment and equipment clean
In the preservation and transportation of fluorosilicone rubber, to prevent dust impurities and rubber contact.
As fluorosilicone rubber has the characteristics of electrostatic dust absorption, so the production environment needs to be purified dust-free workshop, production tools for special equipment. Workers in and out of the operation need to wear clean clothes
Hat. Clean cutting knives, weighing trays and drums of openers. Prevent gloves from contaminating the rubber during the refining process.
2、Mixing and vulcanization
Open the roller temperature of 18 ℃ ~ 28 ℃ when the rubber refining process performance is better. For the use of long-term parking of the rubber material needs to be returned to the refining, to ensure that the material is mixed evenly. Vulcanization molds must be used surface chrome treatment. Fluorosilicone rubber to two-stage vulcanization, in the electric blast box, generally: 200 ℃ x 4 ~ 6 hours.
1, keep the production environment and equipment clean
In the preservation and transportation of fluorosilicone rubber, to prevent dust impurities and rubber contact.
As fluorosilicone rubber has the characteristics of electrostatic dust absorption, so the production environment needs to be purified dust-free workshop, production tools for special equipment. Workers in and out of the operation need to wear clean clothes
Hat. Clean cutting knives, weighing trays and drums of openers. Prevent gloves from contaminating the rubber during the refining process.
2、Mixing and vulcanization
Open the roller temperature of 18 ℃ ~ 28 ℃ when the rubber refining process performance is better. For the use of long-term parking of the rubber material needs to be returned to the refining, to ensure that the material is mixed evenly. Vulcanization molds must be used surface chrome treatment. Fluorosilicone rubber to two-stage vulcanization, in the electric blast box, generally: 200 ℃ x 4 ~ 6 hours.