Due to the high price of fluorosilicone rubber, the rubber is easy to contaminate, thus affecting the performance, so the production of fluorosilicone rubber operation process is extremely strict.
1, keep the production environment, clean equipment
Fluorosilicone rubber in the preservation and transportation process, to prevent dust impurities and rubber contact.
As fluorosilicone rubber has the characteristics of electrostatic dust absorption, so the production environment needs to be purified dust-free workshop, the production of special equipment. Workers need to wear clean clothes and hats to enter and exit the operation. Clean cutting knives, weighing trays and drums of openers. Prevent gloves from contaminating the rubber during the refining process.
2、Mixing and vulcanization
Open the roller temperature of 18 ° C ~ 28 ° C when the rubber refining process performance is better. For long-term parking of the use of rubber materials need to be returned to the refining, to ensure that the material is mixed evenly. Vulcanizing molds must be chrome-plated surface treatment. Fluorosilicone rubber should be two-stage vulcanization, in the electric blower box, generally: 200 ° C x 4 ~ 6 hours.
1, keep the production environment, clean equipment
Fluorosilicone rubber in the preservation and transportation process, to prevent dust impurities and rubber contact.
As fluorosilicone rubber has the characteristics of electrostatic dust absorption, so the production environment needs to be purified dust-free workshop, the production of special equipment. Workers need to wear clean clothes and hats to enter and exit the operation. Clean cutting knives, weighing trays and drums of openers. Prevent gloves from contaminating the rubber during the refining process.
2、Mixing and vulcanization
Open the roller temperature of 18 ° C ~ 28 ° C when the rubber refining process performance is better. For long-term parking of the use of rubber materials need to be returned to the refining, to ensure that the material is mixed evenly. Vulcanizing molds must be chrome-plated surface treatment. Fluorosilicone rubber should be two-stage vulcanization, in the electric blower box, generally: 200 ° C x 4 ~ 6 hours.